High Mechanical Performance Series |
H > Á¦Ç°¼Ò°³ > High Mechanical Performance Series |
|
|
|
Polyester-based thermoplastic Polyurethane(tpu) elastomers
Excellent mechanical properties - tensile strength - low temprrature flexibility - wear resistance - good Processability - recyclability |
|
Product |
Test method |
Unit |
S180A* |
S185A |
S190A* |
S195A |
S198A |
GP55DB |
S160D |
S168D |
Hardness |
ASTM D2240 |
Shore A/D |
83A |
87A |
92A |
95A |
98A/55D |
54D |
63D |
68D |
Specific gravity |
ASTM D792 |
g/§¨ |
1.19 |
1.2 |
1.21 |
1.22 |
1.23 |
1.23 |
1.25 |
1.27 |
Tensile stress at |
ASTM D412 |
|
|
|
|
|
|
|
|
|
at 100% elongation |
|
MPa |
4.5 |
6.5 |
9.5 |
13 |
16 |
16.5 |
22 |
28 |
at 300% elongation |
|
MPa |
9 |
12 |
19 |
28 |
30 |
27.5 |
35 |
40 |
Tensile strength |
ASTM D412 |
MPa |
35 |
40 |
50 |
55 |
50 |
48 |
45 |
45 |
Elongation |
ASTM D412 |
% |
770 |
650 |
650 |
520 |
520 |
530 |
480 |
430 |
Tear resistance |
ASTM D624 |
kN/m |
90 |
110 |
140 |
150 |
180 |
170 |
230 |
250 |
Abrasion resistance |
ISO 4649 |
cc loss |
30 |
30 |
30 |
30 |
25 |
40 |
25 |
25 |
Compression set |
ASTM D395 |
|
|
|
|
|
|
|
|
|
23¨¬C 70hrs |
|
% |
15 |
15 |
15 |
15 |
20 |
25 |
20 |
20 |
70¨¬C 70hrs |
|
% |
35 |
35 |
40 |
40 |
40 |
42 |
45 |
45 |
Mold shrinkage |
ASTM D955 |
mm/mm |
0.02 |
0.01 |
0.009 |
0.008 |
0.008 |
0.008 |
0.007 |
0.006 |
Vicat softening point |
ASTM D1525 |
¡É |
85 |
95 |
110 |
130 |
143 |
124 |
158 |
163 |
|
Suitable for injection molding
(*)UV stabilized grades |